Corrosion fatigue and damage tolerance in the nickel-based superalloy RR1000 subjected to SO2 environments

Martin Bache, Chris Ball, Mark Hardy, Paul Mignanelli

Fatigue & Fracture of Engineering Materials & Structures, Volume: 45, Issue: 5, Pages: 1537 - 1549

Swansea University Authors: Martin Bache, Chris Ball

  • 59482.pdf

    PDF | Version of Record

    © 2022 The Authors. This is an open access article under the terms of the Creative Commons Attribution License

    Download (2.5MB)

Check full text

DOI (Published version): 10.1111/ffe.13687

Abstract

When exposed to a high temperature corrosive environment nickel based superalloys may experience surface pitting and sulphide diffusion, which will influence concurrent or subsequent fatigue behaviour. Sulphur, pre-existing in the environment or as a bi-product of burning fossil fuels, reacts with s...

Full description

Published in: Fatigue & Fracture of Engineering Materials & Structures
ISSN: 8756-758X 1460-2695
Published: Wiley 2022
Online Access: Check full text

URI: https://cronfa.swan.ac.uk/Record/cronfa59482
Tags: Add Tag
No Tags, Be the first to tag this record!
Abstract: When exposed to a high temperature corrosive environment nickel based superalloys may experience surface pitting and sulphide diffusion, which will influence concurrent or subsequent fatigue behaviour. Sulphur, pre-existing in the environment or as a bi-product of burning fossil fuels, reacts with sodium (as an atmospheric pollutant) creating molten sodium sulphate deposits on the metal surface. Combined with sodium chloride, these deposits attack the protective oxide layer allowing sulphides to migrate along grain boundaries. Continued sulphide diffusion promotes a weakened subsurface layer, inducing grain dropout and fatigue crack initiation. The present investigation focussed upon the subsequent effects of exposure to SO2 containing atmospheres on low cycle fatigue performance, together with the impact of an intermediate cleaning process. Damage tolerance data suggest that exposure to a SO2 environment fails to affect fatigue crack growth threshold or stage II growth behaviours when compared with standard laboratory air.
Keywords: damage tolerance; fatigue; hot corrosion; nickel superalloy; pitting