The Study of AA2024 De-Alloying Using Luminol Electrogenerated Chemiluminescence Imaging

Natalie Wint, Z. S. Barrett, G. Williams, H. N. McMurray, Geraint Williams Orcid Logo, Hamilton McMurray

Journal of The Electrochemical Society, Volume: 166, Issue: 11, Pages: C3417 - C3430

Swansea University Authors: Natalie Wint, Geraint Williams Orcid Logo, Hamilton McMurray

  • wint2019(7)v2.pdf

    PDF | Version of Record

    Distributed under the terms of Creative Commons Attribution 4.0 International (CC BY 4.0) License

    Download (2.15MB)

Check full text

DOI (Published version): 10.1149/2.0481911jes

Abstract

This paper describes the use of luminol electrogenerated chemiluminescence (ECL) to image the re-distribution of electrochemically active copper (copper in electrical contact with the substrate) at the surface of AA2024-T351 corroding in NaCl electrolyte. AA2024 samples are thermo-mechanically treat...

Full description

Published in: Journal of The Electrochemical Society
ISSN: 0013-4651 1945-7111
Published: The Electrochemical Society 2019
Online Access: Check full text

URI: https://cronfa.swan.ac.uk/Record/cronfa50771
Tags: Add Tag
No Tags, Be the first to tag this record!
Abstract: This paper describes the use of luminol electrogenerated chemiluminescence (ECL) to image the re-distribution of electrochemically active copper (copper in electrical contact with the substrate) at the surface of AA2024-T351 corroding in NaCl electrolyte. AA2024 samples are thermo-mechanically treated to produce a macroscopically inhomogeneous distribution of intermetallic particles. The AA2024-T351 samples are allowed to corrode by immersion in 0.51 M aqueous NaCl and (ex-situ) ECL measurements are performed to follow copper re-distribution. Luminol ECL light emission is orders of magnitude more intense on copper than aluminum and macro and microscopic images are obtained to elucidate the re-distribution of electrochemically active copper. S phase de-alloying produces a radical re-distribution of copper on a microstructural scale (1-10 μm) but macroscopic copper distributions (1-10 mm) remain largely unchanged. In-situ experiments using the SVET show that macroscopic copper distribution directs localization of corrosive attack such that net anodic activity (pitting/intergranular attack) is concentrated in regions with lowest surface coverage of copper and net cathodic activity is concentrated in regions of highest coverage. Results are explained in terms of the role of solution chemistry and pH in influencing the transition from transient to stable pitting.