Influence of Sn on Deformation Mechanisms During Room Temperature Compression of Binary Zr–Sn Alloys
K. V. Mani Krishna,
D. G. Leo Prakash,
D. Srivastava,
N. Saibaba,
J. Quinta da Fonseca,
G. K. Dey,
M. Preuss,
Leo Prakash 
Zirconium in the Nuclear Industry: 17th Volume, Pages: 138 - 158
Swansea University Author:
Leo Prakash
-
PDF | Accepted Manuscript
Download (2.14MB)
DOI (Published version): 10.1520/STP154320130044
Abstract
Role of Sn on the deformation mechanisms of Zr was investigated undertaking in situ compression loading experiments using neutron diffraction and complementary post mortem electron microscopy. Fully recrystallised binary Zr–Sn alloys, displaying a typical rolling + recrystallisation texture, were st...
| Published in: | Zirconium in the Nuclear Industry: 17th Volume |
|---|---|
| ISBN: | 978-0-8031-7529-7 |
| Published: |
ASTM
2015
|
| Online Access: |
http://www.astm.org/SUBSCRIPTION/DIGITAL_LIBRARY/STP/PAGES/STP154320130044.htm |
| URI: | https://cronfa.swan.ac.uk/Record/cronfa22347 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Abstract: |
Role of Sn on the deformation mechanisms of Zr was investigated undertaking in situ compression loading experiments using neutron diffraction and complementary post mortem electron microscopy. Fully recrystallised binary Zr–Sn alloys, displaying a typical rolling + recrystallisation texture, were studied in situ to determine intergranular strain development, monitor peak intensity changes indicative of twinning, and peak broadening indicative of increased dislocation density. Significant { 101¯2 } 〈 101¯1 〉 type tensile twinning activity was observed for all samples during compression loading. The critical stress for the twin nucleation and the extent of twinning were found to be strongly influenced by the Sn content. Critical plastic strain for the nucleation of twining, however, was observed to be weakly dependent on the Sn content. Results demonstrate significant plastic slip activity to be a necessary condition for the onset of twinning regardless of the Sn content. |
|---|---|
| Keywords: |
Zr–Sn alloys, deformation mechanisms, intergranular strains, twinning, in situ compression, neutron diffraction |